Hi all, thank you very much for your answers! I appreciate this very much! Even if I don't think I have a real Kunitoshi here I will show it to the local nihonto club and will think about a restoration. It's a nice piece and I like it very much.
-
-
-
Wow, thank you so much for your replies. I really appreciate it. Kind regards Christian
-
-
Hi together, thank you for the good replies. As I am also a collector of european swords I am fimilar wird layer pattern in steel, but the structure on this tanto seems to be different, thats why I am asking here.
I added another picture where one can see that these lines are harder areas that stand out from (some long time ago) polishing.
It could be something with different steels but I also have such blades like Sansei was showing and they look pretty different to me.
-
-
Thanks for the link, yes this helps because it explains the difference between chikei as an effect from hardening and as a simple steel layer pattern from mixed steels. I think it is quiet similar to the difference from wootz steel and pattern welded steel.
- 1
-
Hi, thanks for the answers. I already read about chikei but was not aware what it actually is. Is it something what is good to see on blades or is it something what is very common. I just ask because i did not see it on any of my other swords.
-
-
Help with Sayagaki
in Translation Assistance
Posted
Great! Thank you for the fast reply!